Wencon Hi-Temp is a high performance two-component, liquid epoxy coating developed for applications in high load areas. It provides a smooth non porous surface, which is resistant to high temperatures, light chemical aggression and wear as well as bi-metallic corrosion.
Typical applications are coating of surfaces rebuild after deterioration including repair of lining on inert gas systems, fresh water generators, hot pipes and heating coils, protection of tanks, Scrubber outlets, pumps and valves against chemical and mechanical aggression, corrosion and bi-metallic corrosion.
- Good chemical resistance
- High temperature and high abrasion resistance
- Excellent mechanical wear properties
- Strong adhesion to all metal and GRE surfaces
- Fully machinable
| Key technical data |
| Max temperature | +160- +300°C (320 -570°F) |
| Consistency | fluid |
| Mixing ratio vol. | 1:2 |
| Apply with | spatula/brush |
| Potlife at 20°C | 20-40 min. mixed in small amounts |
| Curing time | 10-24 hours |
| Machineability | yes |
| Specific volume | 680 cm3 / kg |
| Dielectric strength | 10 KV/mm |
| Product number | Product name | IMPA no. | ISSA no. |
| No. 1050 | Wencon Hi-Temp, yellow 0,5 kg (1,1 lb) unit | 812345 | 75.553.12 |
| No. 1060 | Wencon Hi-Temp, green 0,5 kg (1,1 lb) unit | 812346 | 75.553.13 |
Wencon Hi-Temp
Wencon Hi-Temp is a high performance two-component liquid epoxy coating developed for applications in high load areas. It provides a smooth non porous surface, which is resistant to high temperatures, light chemical aggression and wear as well as bimetallic corrosion.
Wencon Hi-Temp offers resistance to oil, water, salt water and wide range of acids and alkalis as well as a range of solvents. Heat resistance ranges from 160° C (320°F) in corrosive and heavy load environments and up to 300° C (570°F) when applied as a filling compound.
Wencon Hi-Temp is a double coat system and is consequently.
supplied in two different colors, yellow and green.
APPLICATION AREAS
Wencon Hi-Temp is ideal for protection of tanks, pumps and valves against chemical and mechanical aggression, corrosion and bi- metallic corrosion. Typical applications are coating of surfaces rebuild with Wencon Cream, including repair of lining on inert gas systems, scrubber overboard pipes, fresh water generators, hot pipes and heating coils.
MIXING
The Wencon products are designed to be simple to use and cost effective. Easy mixing ratio (1:2 by volume) reduce waste to a minimum and high specific volume gives high coverage rates.
GENERAL DESCRIPTION
Two-component solvent free liquid epoxy coating for protection against wear, bi- metallic corrosion and chemical aggression at high load areas and temperatures.
SURFACE PREPARATION
The surface must always be dry, clean and degreased.
Applying to new steel surface:
- Grit blasting to SA 2,5
- Profile 75 microns Repairing old steel surface:
- Grit blasting to SA 2,5
- Sweat out water and salts
- Profile 75 microns
MIXING RATIO
Mix by volume 1:2. Mix until an even colour is obtained.
POT LIFE
Depending on amount mixed and tempera- ture. Mixed in small amounts, the pot life is approximately 20-40 minutes at 20°C (68°F)
APPLYING
Wencon Hi-Temp is liquid and is applied by brush, roller or spatula.
OVER COATING
Wencon Hi-Temp is a double coat system. The over coating time can vary from one to three hours depending on temperature. The second coat must be applied whilst the first coat is still tacky. If full curing has occurred a light sandblasting or grinding is necessary prior to the second coat.
CURING TIME
Curing will take place in 10-24 hours at 20°C (68°F)
MACHINABLE
After curing, the product can be machined, drilled and worked like metal.
REDUCED CURING TIME WITH INFRARED
This product is tested with and suitable for infrared curing. Curing with infrared radiation can reduce curing time significantly. Result can vary, depending on circumstances and equipment used.
COVERAGE RATE
Theoretical: 0,86 kg per m2 (0,17 lb/sq. ft.) at 600 microns
Practical: 1,0 kg per m2 (0,20 lb/sq. ft.)
TECHNICAL DATA
Hardness Shore D: 82 (DIN 53505)
Tensile strength: 13,8 N/mm² - 1960 p.s.i. (DIN 53454)
Compressive strength:
Modulus of elasticity: 4284 N/mm² - 610,000 p.s.i. (DIN 53454)
Rcrack: 96 N/mm2 - 14,000 p.s.i. (DIN 53454)
Shear adhesion: 22,40 N/mm² - (ASTM D1002)
Adhesion to steel: 3,4 N/mm² - (ISO 4624)
SPECIFIC VOLUME
680 cm³ per kilogram (41,5 cu inch/kg)
TEMPERATURE RESISTANCE
Corrosion: 160°C (320°F)
Light load: 220°C (428°F)
As filler: 300°C (572°F)
CHEMICAL RESISTANCE
The compound is resistant to oil, water, salt water and most diluted acids and alkalis as well as a range of solvents.
SHELF LIFE
At 20°C (68°F) : 3 years
HANDLING PRECAUTIONS
Read the Wencon Instruction for Use and the Material Safety Data Sheet.
QUALITY TEST
Pretest and test of layer thickness can be tested with normal electronic instrument like high voltage and high frequency.
| Brand | WENCON |
|---|---|
| Product Name | Wencon Hi-Temp |
“Bastini” Co. Ltd.
Department of International Supplies
195279, Sankt-Peterburg, shosse Revolyutcii 69,office 27, Russia
Phone: +7(921) 380 77 97
Email: office@bastini.ru