Wencon Ceramic Coating
Wencon Ceramic Coating is a two-component, liquid epoxy coating suitable for a wide range of applications. It provides a smooth non porous surface, which is resistant to bi-metallic corrosion, light chemical aggression, corrosion and erosion as well as impingement.
Typical applications are coating of surfaces rebuild after deterioration and protection against wear, corrosion and bi-metallic corrosions. Wencon Ceramic Coating has a high abrasion resistance, making it suitable for applications on propeller nozzles, rudders, thruster tunnels and housings. In addition, the product also offer high temperature resistance, which makes it ideal for applications on gas scrubbers, condensers and end-covers.
- Strong adhesion to all metal and GRE surfaces
- High wear resistance
- High temperature resistance
- Efficient double coat system
- High coverage rate
| Key technical data |
| Max temperature | +220- +320°C (428 - 608° F) |
| Consistency | fluid |
| Mixing ratio vol. | 1:2 |
| Apply with | spatula/brush |
| Potlife at 20°C | 20-30 min. mixed in small amounts |
| Curing time | 10-15 hours |
| Machineability | no |
| Specific volume | 658 cm3 / kg |
| Dielectric strength | 10 KV/mm |
| Product number | Product name | IMPA no. | ISSA no. |
| No. 1017 | Wencon Ceramic Coating, light grey 0,5 kg (1,1 lb) unit | 812593 | N/A |
| No. 1018 | Wencon Ceramic Coating, light green 0,5 kg (1,1 lb) unit | 812594 | N/A |
Wencon Ceramic Coating
Wencon Ceramic Coating is a two-component, liquid epoxy coating suitable for a wide range of applications. It provides a smooth non porous surface, which is resistant to bi-metallic corrosion, light chemical aggression, corrosion and erosion as well as impingement.
Wencon Ceramic Coating offers resistance to oil, water, salt water and most diluted acids and alkalis as well as a range of solvents. Heat resistance ranges from 220° C (428°F) in corrosive and heavy load environments and up to 320° C (608°F) when applied as a filling compound.
APPLICATION AREAS
Wencon Ceramic Coating has a high abrasion resistance, making it suitable for applications on propeller nozzles, rudders, thruster tunnels and housings. Typical applications are coating of surfaces rebuild after deterioration and protection against wear, corrosion and bi-metallic corrosions. In addition, the product also offer high temperature resistance, which makes it ideal for applications on gas scrubbers, condensers and end-covers.
Wencon Ceramic Coating is a double coat system and is consequently supplied in two different colors, light grey and light green.
MIXING
The Wencon products are designed to be simple to use and cost effective. Easy mixing ratio (1:2 by volume) reduce waste to a minimum and high specific volume gives high coverage rates.
GENERAL DESCRIPTION
Two-component solvent free liquid epoxy coating for general repair, maintenance and protection of surfaces exposed to excessive wear.
SURFACE PREPARATION
The surface must always be dry, clean and degreased
Applying to new steel surface:
- Grit blasting to SA 2,5
- Profile 75 microns Repairing old steel surface:
- Grit blasting to SA 2,5
- Sweat out water and salts
- Profile 75 microns
MIXING RATIO
Mix by volume 1:2. Mix until an even color is obtained.
POT LIFE
Depending on amount mixed and temperature. Mixed in small amounts, the pot life is approximately 20-30 minutes at 20°C (68°F)
APPLYING
Wencon Ceramic Coating is liquid and is applied by brush, roller or spatula.
OVER COATING
Wencon Ceramic Coating is a double coat system. The over coating time can vary from one to three hours depending on temperature. The second coat must be applied whilst the first coat is still tacky. If full curing has occurred a light sandblasting or grinding is necessary prior to the second coat.
CURING TIME
Curing will take place in 10-15 hours at 20°C (68°F)
MACHINABLE
After curing, the product can be machined, drilled and worked like metal.
REDUCED CURING TIME WITH INFRARED
This product is tested with and suitable for infrared curing. Curing with infrared radi- ation can reduce curing time significantly. Result can vary, depending on circumstances and equipment used.
COVERAGE RATE
Theoretical: 0,91 kg per m² (0,19 lb/sq. ft.) at 600 microns
Practical: 1,2 kg per m² (0,25 lb/sq. ft.)
TECHNICAL DATA
Hardness Shore D: 81
Tensile strength: 25,4 N/mm² - 3614 p.s.i. (DIN 53454)
Compressive strength
Modulus of elasticity: 3030 N/mm² - 431,000 p.s.i. (DIN 53454)
Rcrack: 124 N/mm² - 18,000 p.s.i. (DIN 53454)
Shear adhesion: 28,90 N/mm² - (ASTM D1002)
Adhesion to steel: 4,5 N/mm² - (ISO 4624)
Abrasion Resistance (Taber wear test): 21.9 (ISO 7784-1)
SPECIFIC VOLUME
658 cm³ per kilogram (40,2 cu inch/kg)
TEMPERATURE RESISTANCE
Corrosion: 220°C (428°F)
Light load: 260°C (500°F)
As filler: 320°C (608°F)
CHEMICAL RESISTANCE
The compound is resistant to oil, water, salt water and most diluted acids and alkalis as well as a range of solvents.
SHELF LIFE
At 20°C (68°F) : 3 years
HANDLING PRECAUTIONS
Read the Wencon Instruction for Use and the Material Safety Data Sheet.
| Brand | WENCON |
|---|---|
| Product Name | Wencon Ceramic Coating |
“Bastini” Co. Ltd.
Department of International Supplies
195279, Sankt-Peterburg, shosse Revolyutcii 69,office 27, Russia
Phone: +7(921) 380 77 97
Email: office@bastini.ru